PUTRI, SARAH SWASTI (2016) PEMBUATAN CMC DENGAN MEDIA REAKSI CAMPURAN LARUTAN PROPANOL – ETHANOL DARI ENCENG GONDOK. Other thesis, POLITEKNIK NEGERI SRIWIJAYA.
|
Text
1 COVER.pdf Download (416kB) | Preview |
|
|
Text
11 BAB I PENDAHULUAN.pdf Download (310kB) | Preview |
|
|
Text
12 BAB II TINJAUAN PUSTAKA.pdf Download (846kB) | Preview |
|
![[img]](http://eprints.polsri.ac.id/style/images/fileicons/text.png) |
Text
13 BAB III METODOLOGI PENELITIAN.pdf Restricted to Repository staff only Download (389kB) |
|
|
Text
14 BAB IV HASIL DAN PEMBAHASAN.pdf Restricted to Repository staff only Download (360kB) |
|
|
Text
15 BAB V PENUTUP.pdf Download (184kB) | Preview |
|
|
Text
16 DAFTAR PUSTAKA.pdf Download (305kB) | Preview |
|
|
Text (Data Pengamatan)
17 LAMPIRAN A.pdf Download (333kB) | Preview |
|
|
Text (Perhitungan)
18 LAMPIRAN B.pdf Download (307kB) |
|
|
Text (Gambar)
19 LAMPIRAN C.pdf Download (2MB) | Preview |
Abstract
Making CMC with the reaction media of propanol and ethanol solution mixture from water hyacinth have to find out processing water hyacinthmake into CMC, influence reagent of sodium chloroaceticin making CMC process, and optimun condition as degree of substitution (DS), percentage of purity, viscosity, acidity, and percentage of NaCl to have CMC with the high quality.In this process starting with the pretreatment process/cellulose isolation. Cellulose that obtained was alkalized with 30 % (v/v) NaOH solution. This alkalization process using propanol-ethanol solution mixture as a reaction media. The next process is carboxymethylization process, that happened the reaction between alkali cellulose and sodium chloroacetic with variations of mass 16 gram, 17 gram, 18 gram, 19 gram, 20 gram, 21 gram, and22 gram. From this experiment, obtained influence reagent of sodium chloroacetic sizable in making CMC process. More using sodium chloroacetic make parameter result of CMC analysis advance, among them value of degree of substitution (DS) increase from 0.69 to 0.88, percentage of purity increase from 66.50 % to 86.17 %, viscosity increase from 4.20 cP to 10.20 cP, except acidity of CMC indicated trendentionincrease and decrease that is acidity increase from 7.00 to 10.00 and then acidity decrease to 7.00, while percentage of NaCl that obtained decrease from 33.50 % to 13.83 %. Optimum condition of CMC that obtained at the addition of sodium chloroacetic mass as much as 22 gram. The maximum value of degree of substitution (DS) obtained at0.88, percentage of purity at 86.17 %, viscosity at 10.20 cP, acidity at 7.00, and percentage of NaCl at 13.83 %.
| Item Type: | Thesis (Other) |
|---|---|
| Uncontrolled Keywords: | Alkalisasi, CMC, Enceng Gondok, Karboksimetilasi |
| Subjects: | T Technology > TP Chemical technology |
| Divisions: | Chemical Engineering > Undergraduate Theses |
| Depositing User: | Mrs Trisni Handayani |
| Date Deposited: | 01 Mar 2017 01:54 |
| Last Modified: | 23 May 2017 07:39 |
| URI: | http://eprints.polsri.ac.id/id/eprint/3320 |
Actions (login required)
 |
View Item |